SDI Wave Flowable Composite - Refills

Dental Avenue India Pvt Ltd 28 B Udyog Vihar PhaseV NCR Gurgaon Haryana 122016 India

• Filler Content: Approximately 65% by weight, inorganic filler
• Particle Size: Range from 0.02 to 10 microns for smooth consistency
• Polymerization: Light-cured with visible light (wavelength 400-500 nm)
• Radiopacity: High radiopacity for clear differentiation on X-rays
• Working Time: Optimized to allow precise placement before curing
• Fluoride Release: Sustained release for anti-cariogenic effect
• Shade Range: Available in multiple shades to match natural dentition

• Isolate the operative field to ensure a dry working environment.
• Prepare the cavity according to standard clinical protocols.
• Apply an appropriate dental adhesive system following manufacturer instructions.
• Dispense the flowable composite directly into the cavity using the applicator tip.
• Adapt the material carefully to the cavity walls to avoid voids.
• Light cure the restoration for the recommended duration, typically 20 seconds or as per curing unit specifications.
• Check occlusion and finish the restoration with appropriate polishing instruments.
• Advise the patient on post-operative care and routine follow-up.

• Restorations in small to moderate Class III cavities
• Restorations in Class V cervical lesions, including non-carious defects
• Preventive resin restorations and minimally invasive restorations
• Repair of fractured enamel or composite restorations
• Liner or base under conventional composite restorations
• Sealing of pits and fissures to prevent caries
• Restorations requiring fluoride release for enhanced protection

• Excellent flowability ensures precise adaptation to cavity walls.
• Fluoride release supports enamel remineralization and caries prevention.
• High radiopacity allows easy identification on radiographs.
• Light-cured for controlled working and rapid polymerization.
• Low polymerization shrinkage reduces microleakage risk.
• Versatile use in various restorative and preventive applications.
• Provides durable and esthetic restorations with smooth finish.

Nanofilled
Specially treated nano-fillers enhance polishability, wear resistance, and strength while improving ease of extrusion.

Filler Loading
The high filler loading ensures excellent wear resistance, contributing to durable performance.

Fluoride Release
The cariostatic properties of fluoride promote remineralization and inhibit enamel demineralization. In an aqueous environment, fluoride ions from Wave, Wave MV, and Wave HV diffuse from the resin into the surrounding tooth structure. This ionic transfer is facilitated by oral fluids, which act as carriers for the fluoride ions.

Natural Fluorescene
Incorporates a fluorescent agent for natural-looking teeth under ultraviolet light, ensuring an undetectable, flawless appearance.

Radiopacity
Radiopaque properties make the material easily visible on X-rays, aiding in the identification of secondary caries at the interface.

Compressive Strength
High compressive strength values extend its suitability for a wide range of applications.

UDMA  Resin System
The UDMA resin system minimizes shrinkage and reduces post-operative sensitivity, ensuring patient comfort and clinical reliability.

TIP Length Comparison
Wave’s tip length is 12.2mm—40% longer than the standard 8.7mm. This extended length facilitates precise material placement in hard-to-reach areas.