GC Miracle Mix

GC India Dental Pvt Ltd, NO: 233, Phase 3, Pashamylaram Indl Area, Telangana-502307

POWDER AND LIQUID DISPENSING

• Pour the Miracle Mix alloy into the bottle of Miracle Mix powder and shake thoroughly.
• The recommended powder to liquid ratio is 2 or 3 level scoops of powder to 2 drops of liquid.
• For accurate dispensing of powder, lightly tap the bottle against the hand. Do not shake or invert.
• Hold the liquid bottle vertically and squeeze gently.
• Close bottles immediately after use.
• Shake the powder bottle occasionally.

MIXING

• Dispense powder and liquid onto pad or glass slab. Divide the powder into 2 equal parts. Mix the first portion with all of liquid for 15-20 seconds. Incorporate the remaining portion and mix the whole thoroughly for 20 seconds.

Note : A heavy consistency is recommended.

3. RESTORATIVE TECHNIQUE

• Prepare tooth using standard techniques. Extensive mechanical retention is not necessary. For pulp capping, use calcium hydroxide.
• Wash and dry but do not desiccate. Gc cavity conditioner or Gc Dentin conditioner is recommended to remove the smear layer.
• Mix the required amount of cement. Working time is 1 min. 30 seconds at 23°C (73.4°F). Higher temperatures will shorten working time.
• Remove surface moisture but DO NOT DESICCATE.
• Transfer cement to the preparation using a syringe or suitable placement instrument. Avoid air bubbles.
• Form the contour.
• Setting time is 5’00" to 5’30" from start of mixing.

4. FINISHING

• Use standard techniques

• Core build-up.

• Restoration of primary teeth.

• Cases where radiopacity is required.

• As a base or liner.

• Class I, limited Class II, and temporary fillings.

Strong Chemical Bond: Eliminates the need for undercuts and reduces the use of pins. It will not chip or flake when trimmed or cut.

Simple Technique: Sets in approximately 4 minutes, allowing for efficient procedures.

High Fluoride Release: Helps in reducing secondary caries.

Aesthetic Considerations: Does not stain or discolor surrounding teeth and is easily distinguishable from the tooth structure.

Physical Properties: Exhibits similar shrinkage and expansion characteristics to natural tooth structure.