GC Fuji 9 GP Extra Capsules

GC India Dental Pvt Ltd, NO: 233, Phase 3, Pashamylaram Indl Area, Telangana-502307

Fuji IX GP EXTRA Capsule
Mixing Time (sec) 10”
Working Time (min, sec) 1’15”
Finishing begins (from start of mix) 2’30”

* Mixing conditions at 23°C. Higher temperatures will shorten working time.

• After conditioning the tooth surface with GC Dentine Conditioner (10% polyacrylic acid), apply the Gold Label 9 or Fuji IX GP in Capsule mixed accordingly into the cavity
• Form the contour and place a matrix if required during the working time
• After initial set, when the material starts to lose the glossy appearance, moisture protectwith GC Cocoa Butter or GC Fuji Varnish or GC Fuji Coat LC
• Final finishing under water spray can be carried out at the recommended times from start of mix
• After finishing, apply a final coat of GC Fuji Varnish or GC Fuji Coat LC as a protective coating. Alternatively, application of a final protective coat of G-Coat PLUS can improve wear resistance

• Class I and small Class II restorations in non-load bearing areas
• Class I and Class II restorations in deciduous teeth
• Transitional restorations
• Base / Core build-ups

• Chemical adhesion to tooth structure allows minimal cavity preparation without the need for etching or bonding agents
• Chemical setting without shrinkage allows single step placement without layering
• Similar thermal expansion as tooth structure produce minimal stress on the marginal seal
• Strontium based glass provides good radiopacity and snap-set characteristics unanimously preferred by clinicians
• Strontium based fluoride releasing formulation contributes to internal remineralization within tooth structure as well as increasing surface strength over time
• High compressive and flexural strength, and 60% higher wear resistance than conventional glass ionomers makes Gold Label 9 strong enough for use in posterior teeth
• Faster, easier and more efficient placement
• No measuring as powder and liquid are pre-measured in the right ratio
• Mechanical mixing leads to less porosities and a stronger mix
• Extra fluoride release
• Extra fast setting yet with ample working time
• Extra translucency for improved aaaesthetics